Q:- The exposed surfaces of each fillet-weld-break specimen shall show:

1. No Slag inclusions greater than 1/4 inch
2. At least 3/4 inches sound metal between adjacent inclusions
3. Complete penetration and fusion
4. The tensile strength of the specimen
5. None of the above

Q:-When considering the advantages of site RT over UT which of the following applies?

1. A permanent record produced, good for detecting defects which do not have significant depth in relation to axis of the X-ray beam and defect identification 
2. A permanent record produced, good for detecting all surface and sub-surface defects and assessing the through thickness depths of defects 
3. A permanent record produced, defect identification not so reliant on operator skill 
4. No controlled areas required on site, a permanent record produced and good for assessing the extent of pipe wall thickness reductions due to internal corrosio 

Q:- When pipe is welded above ground, the working clearance around the pipe at the weld should be at least:

A. 12 inches 
B. 16 inches 
C. 20 inches 
D. 24 inches 
E. 30 inches

Q:- One the advantages of ultrasonic inspection in relation to radiographic testing to;

A. Access is generally only required from one side (surface)of the component being tested
B. The designated work area must be closed off by barriers, therefore safety is increased
C. This materials can be easily examined
D. A permanent image of the defect can be obtained 

Q:-During welder qualification, when destructively testing pipe with a diameter less than or equal to 33.4 mm:

1. Radiography must be used
2. The entire pipe must be used for bend testing
3. One full-section tensile specimen may be substituted for the root-bend and nick-break 
specimens. 
4. Pipe of this diameter may not be destructively tested e. none of the above 

Q:- Which of the following is not the reason for the increase of HAZ cracking when welding carbon manganese steels?

1. Fast cooling after welding
2. High manganese content
3. High carbon content
4. None of the above

Q:- A medium carbon steel weld shoukd be inspected:

1. As soon as it is safe to do so
2. When the weld is finished
3. 48hrs after the completion
4. After ndt examination

Q:- The correct term for a joint prepared on one component only is:

1. A Bevel Butt  
2. A J Butt  
3. A K Butt  
4. All of the Above 

Q:- What is meant by the term junction?

1. The area containing the HAZ and the weld metaL
2. The weld metal and parent metal
3. The boundery between the fusion zone and the HAZ
4. The part of the weld, has undergone mettalurgical changes due to the heat from welding

Q:- A magnifying glass may be used during visual inspection but BS 5289 states that its magnification should be:

A. Up to 5  
B. 2 - 2.5  
C. 5 - 10  
D. None of the Above 

Q:- When 2 different material types are welded together, the joint may be referred to as

A. A Composite Joint
B. A transition Joint
C. A Dissimilar Metal Joint
D. Either B or C 

Q:- Quality Assurance:

1. Another name for inspection
2. Relates to all activities and functions concerned with the attainment of quality
3. Is the activity of ensuring documents related to specific contracts are in order
4. Is the activity of carrying out quality control

Q:- The correct term of cap height is:

1. Reinforcement  
2. Cap profile height  
3. Excessive weld metal  
4. All of the Above

Q:- Under most circumstances, which of the following do you consider to be duties of a welding inspector?

1. The supervision of welders  
2. Procedure writing  
3. Qualifying welders  
4. All of the Above

Q:- For procedure qualification, the exposed surfaces of each nick-break specimen shall show:

1. No slag inclusions over 1/4 inch 
2. At least 3/4 inches of sound weld metal between inclusions 
3. Complete penetration and fusion 
4. The tensile strength of the sample 

Q:-Which joint type for more susceptible for stress?

1. Single v but 
2. Double v but 
3. Compound weld 
4. Cruciform joint

Q:- For pipe ends of the same nominal wall thickness, the alignment offset requirement is:

1. Not more than 1/4 inch
2. Not more than 1/8 inch 
3. Not more than 1/32 inch 
4. If misalignment is larger than 1/16 inch due to dimensional variations, it shall be equally 
distributed around the circumference of the pipe.
5. None of the above

Q:- MIG/MAG welding what would be affected if the CROWD was extended?

1. Amperage
2. Voltage
3. Inductance
4. Travel speed 

Q:- Which one of the following codes/ standards is not a qualification code?

 1. ASME section IX  
 2. AWS D1.1  
 3. EN ISO 15614  
 4. ASME B31.3 

Q:- For welder qualification, the specimens shall be prepared for tensile-strength, nick-break, and bend tests. When tensile-strength tests are omitted:

1. The welder is not qualified 
2. The weld must be redone 
3. The is not covered in API 1104 
4. Tensile-Strength specimens shall be subject to the nick-break test 
5. Extra face bends must be tested